Zinc Rich
Zinc Clad II Ethyl Silicate, Inorganic
ZINC CLAD II ETHYL SILICATE is a solvent-based two-package, inorganic ethyl silicate, zinc-rich coating.
- Meets Class B requirements for Slip Coefficient and Creep Resistance, .56
- Meets AASHTO M-300 specification
- 85% zinc content in dry film
- Coating self-heals to resume protection if damaged
- Provides cathodic/sacrificial protection by the same
mechanism as galvanizing. Also protects steel by forming an inorganic moisture and solvent barrier
Recommended Usage
For use over properly prepared blasted steel.
- As a one-coat maintenance coating or as a permanent primer for severely corrosive environments (pH range 5-9)
- Economical replacement for galvanizing with similar performance
- Ideal for application at low temperatures or service at high temperatures and/or humidity conditions
- Water intake and discharge lines (non-potable)
- Where abrasion resistance and hardness is required
- Bridges, refineries, drilling rigs
- Shop or field application
- Not recommended for severe acid or alkali exposure